Production and Characterization of Alumina Zircon Refractory: Using a Clay Binder
Student: Rachael Tiam (Project, 2025)
Department of Glass Technology
Ahmadu Bello University, Zaria, Kaduna State
Abstract
This study investigates the production and characterization of alumina-zircon refractory composites using a clay binder, focusing on the effects of clay content on micro-structure, mechanical, and thermal properties. Alumina (Al2O3) and zircon (ZrO2) powders were mixed with varying amounts of clay binder (5-15 wt%) and sintered at 1400°C. The physical and mechanical properties of the composites were evaluated using Porosity and mechanical strength testing. Samples 2 and 3 which had 10 & 12% Clay content showed the highest MOR and Porosity scores. While the samples with 5 and 15% clay content showed less Porosity and MOR. This goes to show the importance of optimal binder percentage.
Keywords
For the full publication, please contact the author directly at: tiamrachael@gmail.com
Filters
Institutions
- Redeemers University, Ede, Osun State 4
- Rhema University, Aba, Abia State 11
- Rivers State University of Science and Technology, Port Harcourt, Rivers State 3
- RIVERS STATE UNIVERSITY, PORT HARCOURT, RIVERS STATE 13
- Rufus Giwa Polytechnic, Owo, Ondo State 2
- Saadatu Rimi College of Edu, Kumbotso, Kano State (affiliated To Abu, Zaria) 1
- Salem University, Lokoja, Kogi State 4
- School of Health Information Mgt (Uch, Ibadan), Oyo State 5
- School of Health Information Mgt, Oau Teaching Hospital, Ile-Ife, Osun State 30
- Skyline University Nigeria, Kano, Kano State 2